Ka ɲɛsin dip galvanized galonized pallvanized ma, min be baara kɛ ni kuran yɛlɛmani yɔrɔw ye, hot-dip galvanizasiyɔn baarakɛcogo be se ka kɛ ka ɲɛ. Nin barokun bena kunnafoni dɔw di ka bɔ baarakɛcogo sariyaw, baarakɛcogo jɔnjɔnw, baarakɛcogo ɲumanw kɔlɔsili yɔrɔw, baarakɛcogo nafaw ani jamana wɛrɛw ka jago sariyaw labatoli sariyaw.
Hot{{0}dip galvanizasiyɔn ye nɛgɛ ɲɔgɔndan yɛlɛmani ye. Ni nɛgɛ nɛgɛlaman dɔ be sɔrɔ zɛnki mugu la min be se ka yɛlɛma degere 450 ɲɔgɔn na , nɛgɛ (Fe) nɛgɛ ka yɔrɔ la ani zɛnki (Zn) min be sɔrɔ zɛnki mugu kɔnɔ, o be to ka jɛnsɛn ani ka yɛlɛmani don a la, o min be kɛ saba ye -. Ka bɔ a kɔnɔna na, o yɔrɔw ye:
Iron{{0}ZinZin Layer (Inner Layer): A be ɲɔgɔn minɛ ni nɛgɛ ye, a fanba be kɛ ni Fe3Zn10 ni FeZn7 ye, a ka ca ani a be ɲɔgɔn minɛ kosɔbɛ, a be garanti jɔnjɔn di galvanizen ka yɔrɔ la.
Zinc{{0}Iron Alloy Layer (Cɛmancɛ Layer): FeZn13 be sɔrɔ a la, a ka bon dɔɔni ani a be gɛlɛya ni gɛlɛya fara ɲɔgɔn kan.
Zinc Layer san (Sugandilikɛla): Ka kɛnɛma yɔrɔ datugu, a ka nɔgɔ ani a be yɛlɛma, a be kɛ zɛnki oksidi latanga filimu ye min be mɔgɔ latanga. Ka fara o kan, ni yɔrɔw be yɔrɔ dɔw la, a be to ka yɔrɔ min sɔgɔ, o be to ka yɔrɔ min sɔgɔ, o be se ka kɛ sababu ye ka yɔrɔ min sɔgɔ, o sababu fɛ.
Hot Dip Galvanized yoke plates, saba ka kan ka kɔlɔsi ka ɲɛ ka tɛmɛ 65 μm kan. O la, a be se ka caya ka se 85μm ma walisa ka se ka kɔgɔ caman ni yɔrɔw nɔgɔya minw be se ka nɔgɔ.
O la, a ka kan ka tugu furakɛli ɲɛ - hot-dp galvaniding - furakɛli kɔfɛ - sɛgɛsɛgɛli la. O la, furakɛli min be kɛ ka kɔn, o lo ye fɛɛrɛ jɔnjɔn ye min b’a yira cogo min na a be se ka mɔgɔw lasun u ka fani don ani k’a to u be se ka nɔrɔ ɲɔgɔn na ani k’u kɛ kelen ye.
Furakɛcogo: I ka baara kɛ ni alkali ye min be se ka jigi 60-80 degere la miniti 5-10 la, walima ka baara kɛ ni fɛn ye min be se ka kɛ ka tulu bɔ, ka tulu bɔ, buguri ni tulu nɔgɔ ka bɔ nɔrɔnɔrɔnin sanfɛ. O yɔrɔ minw be ni mugu ye, ani boli dingɛw kɔnɔ kogow ye yɔrɔ minw ye, u be se ka kɛ ka tulu to yen, o min be se ka kɛ ka mɔgɔw farikolo yɔrɔ dɔw sɔgɔ wagati jan kɔnɔ wala k’u saniya ni ultrasonic ye.
Jii ko ani k’a saniya: Aw b’a ko ni jii koyɔrɔ fɔlɔ ni filanan ye walisa ka fɛn tɔw bɔ. O baara ka kan ka kɛ ko jii be lajɛn wala ko a tɛ se ka kɛ bolokɔn dingɛw kɔnɔ.
Asidi pickling ani nɔgɔ bɔli: Asidi idɔrɔkloriki kɛ ka mugu tigɛ, ka yɛlɛma so kɔnɔ miniti 10 kɔnɔ walisa ka oksidi sɛgɛsɛgɛli, nɔgɔ, ani oksidi yɔrɔ yɛlɛma ka bɔ yoke plate sanfɛ. Ka ɲɛsin oksidi hakɛ ma, pickling wagati be se ka janya ka ɲɛ, nka a ka ɲi ka sɛgɛsɛgɛri kɛ walisa a kana yɛlɛma ka tɛmɛ, o be se ka kɛ sababu ye ka yɔrɔw nɔgɔya ani ka nɔrɔli dɔgɔya.
Jii ko ani k’a nɔgɔya: A’ y’a to a be se ka kɛ ko a be se ka kɛ ko a be se ka kɛ ko a be se ka yɛlɛma. Bolt dingɛw kɔnɔ kogow ka kan ka ko ka ɲɛ walisa asidi tɔw kana kɛ sababu ye ka yɔrɔ min be nɔgɔ bɔ, o ka se ka yɛlɛma.
Drying and preheating: Dry at 120-150℃ for 10-15 minutes to completely remove surface moisture. The surface must be free of water stains and oxidation; otherwise, the galvanized layer may show signs of blistering or exposure to oxidized material. Defects such as those mentioned above; Zinc immersion: The zinc immersion temperature is strictly controlled at 445-460℃. The immersion time is adjusted according to the thickness of the plate. When the thickness is ≤6mm, the immersion time is 1-2 minutes. When the thickness is >6mm, n’i be jigi wagati min na, o ye miniti 2-3 ye. Nɛnɛ furakɛli: I ka fiɲɛ nɛnɛ wala jii bugun ta ka nɛnɛ ka se so kɔnɔ funteni ma. Nɛnɛ wagati la, i kana ɲɔgɔn gosi Hot Dip Galvanized Yoke Plates cɛ walisa a kana yɔrɔw sɔgɔsɔgɔ.
Hot Dip Galvanized Yoke Plates minw be bɔ jamana wɛrɛw la, u ka kan ka bɛn ni sariyaw ye minw ɲɛsinna sugu laɲinin ma; N’o tɛ, u tena se ka don sugu la. Komi an ye baarakɛla ŋana ye, an ka baarakɛyɔrɔ be fɛɛn ɲumanw lo bila a ɲɛfɛ; i kana sigasiga k’a san.